過飽和固溶体の英語

又、合金材は実質的に平均結晶粒径が１００ｎｍ〜１０μｍのα−Ａｌの過飽和固溶体単相からなる。例文帳に追加

The alloy material is composed essentially of α-Al supersaturated solid solution single phase of 100 nm-10 μm average crystal grain size. - 特許庁

また、実質的に平均結晶粒径が１００ｎｍ〜１０μｍのα−Ａｌの過飽和固溶体単相からなることが好ましい。例文帳に追加

Furthermore, it is preferably formed of an α-Al supersaturated solid solution single phase substantially of 100 nm to 10 μm average crystal grain size. - 特許庁

また、実質的に平均結晶粒径が１００ｎｍ〜１０μｍのα−Ａｌの過飽和固溶体単相からなることが好ましい。例文帳に追加

Moreover, preferably, it is substantially composed of an α-Al supersaturated solid solution single phase of 100 nm to 10 μm average crystal grain size. - 特許庁

この溶体化処理部２０によれば、析出硬化型元素を過飽和に固溶する固溶体を得るのに必要な急冷をすると同時に、形状と表面状態の良好な析出硬化型合金薄帯を得ることができる。例文帳に追加

By this solution treatment part 20, rapid cooling required for obtaining a solid solution in which precipitation hardening type elements perform solid-solution in a supersaturated state is performed, and simultaneously, the precipitation hardening type alloy thin strip having the satisfactory shape and surface conditions can be obtained. - 特許庁

ＡｌにＳｉ、Ｇｅ等を平衡状態の固溶限を越えて添加した合金とＮｂとの複合線材において、複合線材のままの状態で急熱急冷処理することにより、Ａｌ合金芯を過飽和の固溶体に変える。例文帳に追加

This manufacturing method includes subjecting a composite wire rod consisting of an Al alloy containing more Si and Ge than the solid solubility limit in the equilibrium state and Nb, to rapid heating and quenching treatment in the state of the composite wire rod, to change an Al alloy core into a supersaturated solid solution. - 特許庁

鉄系合金部材とアルミニウム系合金部材を溶接により接合した異種金属溶接接合体であって、前記鉄系合金部材と前記アルミニウム系合金部材の溶接接合部が、鉄にアルミニウムが過飽和に固溶した過飽和固溶体相を含む組織からなることを特徴とする鉄系合金部材とアルミニウム系合金部材の異種金属溶接接合体。例文帳に追加

This joined body obtained by joining the iron based alloy member and the aluminum based alloy member by welding is characterized in that the joint part between the iron based alloy member and the aluminum based alloy member has a structure including a supersaturated solid solution phase in which aluminum enters into solid solution in iron in a supersaturated manner. - 特許庁

１ａｔ％以上、７．５ａｔ％以下のチタンを固溶させた銅−チタン合金を急冷し、得られた過飽和固溶体銅−チタン合金を冷間圧延した後、時効析出硬化させ、かつ水素を含有させる、銅−チタン−水素合金の製造方法が提供される。例文帳に追加

In the method for producing a copper-titanium-hydrogen alloy, a copper-titanium alloy in which titanium of 1 to 7.5 atom% is made to enter into a solid solution is rapidly cooled, the obtained supersaturated solid solution copper-titanium alloy is cold-rolled, and is thereafter subjected to age precipitation hardening, and also, hydrogen is incorporated therein. - 特許庁